Product Data
- Fast dry, dry to touch in 2 hours at 70°F (21°C)
- Recoat in 3 hours at 70°F (21°C)
- Low temperature cure down to 0°F (-18°C)
- Exceptional corrosion protection in industrial and marine corrosive environments
- Surface tolerant, excellent adhesion to tight rust and prepared damp surfaces
- Self priming topcoat over most existing coatings
- Can be overcoated with a wide range of topcoats
- Temperature resistance to 450°F on insulated or uninsulated surfaces when mixed with Amercoat 880 glass flake additive.
| VOC Amlerlock 2 |
lb/gal |
g/L |
| mixed |
1.5 |
180 |
| mixed/thinned (1/2 pt/gal) |
1.8 |
216 |
|
| VOC Amerlock 2AL |
lb/gal |
g/L |
| mixed |
1.0 |
123 |
| mixed/thinned (1/2 pt/gal) |
2.0 |
234 |
|
| Volume solids (ASTM D2697 modified) |
|
| Amerlock 2 |
85% ±2% |
| Amerlock 2AL |
85% ±3% |
Amerlock 2's low solvent level meets most VOC requirements, reduces the chances for film pinholing and solvent entrapment at the substrate-coating interface, often a major cause of coating failure with conventional epoxies and lower solids systems. Amerlock 2 is available in a variety of colors, and therefore does not require a topcoat. For extended weatherability or special uses, a topcoat may be desired.
Typical Uses
Amerlock 2 is designed for use in a variety of areas, even those where surface preparation is impossible. As a maintenance coating, Amerlock 2 protects steel structures in industrial facilities, bridges, tank exteriors, marine weathering, offshore, oil tanks, piping, roofs, water towers and other exposures. Amerlock 2 has good chemical resistance to splash/spillage, fumes and immersion in neutral, fresh and salt water (see resistance table). Contact your PPG representative for specific information.
Qualifications (Amerlock 2)
1.USDA - Incidental food contact
2.NSF Standard 61* - For use in drinking water.
3.FDA 21 CFR 175.300 extraction
Topcoats
Amercoat 450 Series Amershield, PSX 700, PSX 1001
Primers
Dimetcote 9,Dimetcote 302H, Amercoat 68 Series, Self Priming
Click here for Product Data Sheets