ABC #3 quick reference

Components 1
Curing mechanism	Solvent release
Volume solids	56% ± 3%
(ASTM D2697, modified)
(ASTM D2697, modified)
Coats	2 or 3
Dry film thickness per coat	4-6 mils (100-150 microns)
Theoretical coverage	ft²/gal	m²/L
1 mil (25 microns	898	22.0
4 mil (100 microns	224	5.6

Environmental Conditions
Temperature	°F	°C
Air and Surface	0 to 120	-18 to 49
Surface temperatures must be at least 5°F (3°C) above dew point to prevent condensation.
Drying and cure time @ 4 mils (100 microns) (hours) Temperature, °F/°C 120/49 90/32 70/21 50/10 32/0 recoat 1 3 5 10 20 Before immersion 3 4 6 12 20 max recoat time not restricted max to launch not restricted
Equipment Cleaner	T-10

Application Procedure
1.	Clean all application equipment with T-10.
2.	Stir material thoroughly and continue stirring during application to insure pigment suspension.
3.	Thin only for workability; no more than 10% by volume .
4.	Apply a wet coat in even, parallel passes; overlap each pass 50 percent to avoid pinholes, bare areas or holidays. Give special attention to weld seams, rough or badly pitted areas. If required, cross spray at right angles.
5.	For touch-up and repair, apply additional material after removing dirt, contaminants or old loose coatings or antifoulings.
6.	Allow 4 hours drying time at 70°F (21°C) before applying second coat.
7.	Before immersing, allow ABC 3 to dry at least 6 hours at 70°F (21°C).
8.	Clean application equipment immediately after use with T-10.

Full Product Data Sheets

Return to quick reference index